bal·las 英'bæləs美'bæləs COCA¹⁸⁰⁴⁵⁰
基本例句
n.半刚石¹⁰⁰原型balla的复数 And Mr. Ballas was the inventor of the Weed Eater.
此外，巴拉斯先生还是手持式割草机的发明人。 hjenglish
Applying polycrystalline ballas diamond as material for high- duty, thin coating surfaces on suitable substrates with even complex pre- shaped geometries should be quite easy.
在具有更为复杂的预成形几何形状的适当基体上将聚晶半刚石用作高强度薄涂层表面材料应当说是很容易的事情。 yanyu-trans
George Ballas became known as the “ Weed King”.
乔治•巴拉斯以“除草大王”而闻名世界。 yeshj
It must be noted that the Raman intensity background increases strongly due to the morphological change from faceted to ballas diamond.
必须注意的是，拉曼强度背景因形貌从多面金刚石变成半刚石而得到明显的提高。 sanways
The formation of ballas is observed with increasing carbon supersaturation CH4 content in the gas phase respectively with decreasing at. H/ C ration.
随着 H/ C比率减小，气相中碳的超饱和度 CH4含量相应增大，从而形成半刚石。 yanyu-trans
The ballas type grown at the transition to the graphitic deposition is characterized by a homogenous micro- twinned matrix.
在向石墨沉积转变中生成的半刚石种类的特征是均匀的显微孪晶基体。 sanways
Ballas was the inventor of the Weed Eater.
而B现实是吃草机的发明者。 hjenglish
After passing a maximum a decreased growth rate for ballas deposition occurs Fig.2.
超过最大含量后，半刚石沉积的生长速率减小图2。 yanyu-trans
Due to this fact with increasing distance from the hydrogen source ballas deposition occurs Fig.3.
因此，随着与氢源距离的增大，发生半刚石沉积图3。 yanyu-trans
From the present point of view the ballas morphologies can be described by various microstructures.
按照目前的观点，半刚石的形貌可通过多种显微结构加以描述。 yanyu-trans
George Ballas of Houston, Texas, lived a long life.
德克萨斯州休斯敦的乔治·巴拉斯 George Ballas走过了漫长人生。 ebigear
George Ballas was born in Louisiana. He joined the military at seventeen. He served in World War Two and the Korean War.
George Ballas在路易斯安那出生，17岁参军，曾参加第二次世界大战和朝鲜战争。 hxen
George Ballas was born in Louisiana.
巴拉斯出生于路易斯安那州。 hjenglish
In 1952, George Ballas married Maria Louisa Marulanda, a Spanish Flamenco dancer and film actress.
1952年，乔治•巴拉斯与西班牙弗拉门科民歌舞者兼电影演员玛利亚•路易莎•马路兰达结婚。 hjenglish
In 1952, George Ballas married Maria Louisa Marulanda, a Spanish Flamenco dancer and film actress. They were together for59 years until his death.
1952年，乔治•巴拉斯与西班牙弗拉门科民歌舞者兼电影演员玛利亚•路易莎•马路兰达结婚。他们的婚姻持续了59年，直到他的离世。 yeshj
In order to use the high potential of the unique ballas structure in industrial applications further investigations should be performed on the low-pressure ballas synthesis.
为了在工业应用中发挥独特半刚石结构的巨大潜能，须对低压半刚石合成进行进一步的研究。 yanyu-trans
In the present work the facts of ballas diamond deposition will be summarized and correlated with the described nano- crystalline diamond.
本文对半刚石沉积的实际情况进行了综述，并将它们与所述纳米晶金刚石联系起来。 yanyu-trans
In detail the microstructures shown by TEM for the nano- and ultranano- crystalline diamond can also be observed in ballas diamond.
TEM显示的纳米和超纳米晶金刚石显微结构在半刚石中也能看到。 yanyu-trans
In all cases Raman spectra showed clearly the formation of the ballas diamond.
就一切情况而论，拉曼光谱明显反映了半刚石的形成。 yanyu-trans
In flat ballas the D- band is smaller and the graphite peak larger than in coarse ballas.
在扁平的半刚石中， D带较小，而石墨峰比粗大的半刚石中的要大。 yanyu-trans
It could be shown that ballas diamond, nano- crystalline diamond and ultranano- crystalline diamond are very similar materials.
可以看出，半刚石、纳米晶金刚石和超纳米晶金刚石是十分相似的材料。 yanyu-trans
The addition of foreign gases like N2, PH3 or boron compounds, etc. can change the diamond morphology from faceted to ballas with increasing concentrations.
加入诸如 N2、 PH3或硼化合物等外部气体能使金刚石的形貌随着各含量的增加从多面金刚石变成半刚石。 yanyu-trans
The described nano- crystalline diamond deposits show nearly the same Raman peaks as ballas deposits and also the TEM images look very similar.
上述纳米晶金刚石沉积物显示出与半刚石沉积物几乎相同的拉曼谱峰，而且 TEM图象也十分相似。 yanyu-trans
This is a guest post by Nadia Ballas- Ruta of Happy Lotus.
本文是纳迪娅巴拉斯-露塔的帖子，来自幸福莲花。 kekenet
This was observed by diamond deposition on iron substrates where, due to the high vapor pressure of iron, ballas is formed at methane concentrations lower than0.4%.
这一点是在铁基体上沉积金刚石时发现的。这时，由于铁的蒸汽压力很高，在甲烷浓度低于0.4%时可形成半刚石。 yanyu-trans
Transition from ballas-like morphologies to layers containing graphitic inclusions is initialized by implementation of fine lamella.
由半刚石形貌到含有石墨杂质的涂层的转变是从细晶薄层开始的。 yanyu-trans
With decreasing substrate temperature, the domain boundaries marking the transition between faceted and ballas morphologies extend to higher methane concentrations in the gas phase Fig.4.
随着基体温度的下降，标志多面金刚石和半刚石形貌转变的区域边界延伸至甲烷含量较高的地方图4。 sanways
Ballas is a non- faceted, polycrystalline spherically grown diamond having a radial structure.
半刚石是一种具有径向结构的非多面、聚晶球状金刚石。 yanyu-trans
Ballas is nearly pure diamond with nano- crystalline structure.
半刚石几乎是具有纳米晶结构的纯金刚石。 yanyu-trans |