| 释义 |
pitting corrosion短语¹⁸⁰⁰⁹⁸⁺¹
基本例句
孔腐蚀,麻点状腐蚀,点蚀
An analysis of the cause of pitting corrosion failure of heat exchange coil is made by means of X-ray energy spectrometer in this paper.
利用化学分析和 X射线能量色散谱等方法，对换热器盘管孔蚀的原因进行了分析。 cnki
It was found from the analysis and study of the corrosion failures of refinery storage tanks that the pitting corrosion was the major cause of the failure.
通过对炼油厂储罐腐蚀失效形式的调查分析，得出局部腐蚀是导致储罐失效的主要原因。 cnki
The electrochemical characteristics of pitting corrosion of X70 pipeline steel in phosphate buffer solution were studied in this paper.
研究了 X70钢在磷酸盐缓冲溶液中的亚稳态与稳态孔蚀的电化学行为特征。 dictall
The induction time for pitting corrosion of the18-8 stainless steel in neutral chloride solution is determined by potentiostatic technique.
用恒电位法测定了18-8不锈钢在中性氯离子溶液中孔蚀的诱导时间。 jmonline
The influence of different heat treatment technologies on uniform corrosion, intergranular corrosion, pitting corrosion and electrochemical corrosion properties is emphatically studied.
着重研究了不同热处理制度对铸造高性能合金的均匀腐蚀、晶问腐蚀、点蚀和电化学腐蚀性能的影响。 cnki
The mechanism of porous oxygen electrode to accelerate pitting corrosion of bronze ware has been put forwarded.
提出了加速青铜器小孔腐蚀的多孔氧电极机理。 cnki
The pitting corrosion of the fresh stainless steel surface have been studied.
研究了不锈钢去膜表面在氯化镁介质中的点腐蚀现象。 cnki
But the seawater of Xiamen inhibits the pitting corrosion of Cu-Ni alloys, so that no pitting corrosion is observed on Cu-Ni alloy plates tested there.
而厦门海域对铜镍合金的局部腐蚀有一定的减缓作用，使铜镍合金板材没有局部腐蚀发生； www.csu.edu.cn
By determinations of pitting potentials, re passive potentials and pitting critical concentrations of Cl-, the resistance to pitting corrosion was evaluated.
通过测定点蚀电位再钝化电位和点蚀临界氯离子浓度等参数来评定体系的抗点蚀性能。 journal.ecust.edu.cn
Development of scanning tunnel microscopySTM is reviewed in brief. Application of STM in researching local corrosion, pitting corrosion and passive films on metals is introduced emphatically.
简述了扫描隧道显微镜技术的发展概况，着重介绍了扫描隧道显微镜在局部腐蚀、 点蚀、钝化膜形成等方面的应用。 chemyq
Morphology of corrosion presents pitting corrosion character.
腐蚀形貌呈现孔蚀特征。 cnki
The results show that its pitting corrosion resistance is superior.
结果表明，该钢具有优良的耐点蚀性能。 cnki
The results show, when pitting corrosion occurred on the brass surface, the polarization resistance of electrode was obviously decreased, and the corrosion potential being also obviously lowered.
结果表明，黄铜表面出现点蚀时，电极的极化电阻明显下降，腐蚀电位也明显降低。 cnki
The results indicate that the holes of X70 pipeline steel result from pitting/span> corrosion. And the appearance of the pitting corrosion is because of high concentration of Cl- in laminar- cooling water.
实验结果表明， X70管线钢凹坑是由于点蚀腐蚀所引起，而点蚀产生的原因是由于层流冷却水中的氯离子浓度偏高。 rjggy.net
The results indicated that the resistance to pitting corrosion of mild steel inhibited by molybdate is better than by nitrite.
实验结果表明：钼酸盐比亚硝酸盐对软钢有更好的抗点蚀性能。 journal.ecust.edu.cn
The submerged coupon simulation tests also confirm that sulfate reduction bacteria can also cause magnesium alloy corrosion, which features pitting corrosion.
采用浸泡挂片模拟实验进行研究，发现硫酸盐还原菌可以引起镁合金腐蚀，且腐蚀特点为点蚀。 chemyq
The surface roughness, pitting corrosion, burn and hydrogen uptake of ECM machined Ti- alloy blades are analyzed and the measures of improving surface integrity are introduced.
本文就钛合金叶片电解加工后的表面粗糙度、点蚀、烧伤及吸氢等问题进行了分析并提出了改善钛合金电解加工表面完整性的措施。 cnki
The pitting corrosion potential of316 stainless steel increases along with the ammonia nitrogen density decrease.
在模拟中水中，随着氨氮浓度的增加，316不锈钢的孔蚀电位减小。 cnki
Pitting corrosion and crevice corrosion in catalyst deposit zone and corrosion deposit zone can also induce stress corrosion cracking.
催化剂沉积区和腐蚀产物沉积区产生的点蚀和缝隙腐蚀会诱发应力腐蚀开裂的产生。 cnki
Pitting corrosion of steam turbine blading steels: the influence of chromium content, temperature, and chloride lon concentration.
铬含量、温度和氯化物浓度对蒸汽轮机叶片钢点蚀的影响。 kuenglish |