| 释义 |
cement paste短语¹¹⁴⁴⁶⁷⁺⁴
基本例句
水泥浆
In the constructing of duct grouting for post- tensioning bonded prestressed concrete, the suitable cement paste is the most essential and important factor to guarantee grouting quality.
在后张有粘结预应力砼孔道灌浆的施工中，良好性能的水泥浆体是保证灌浆质量的最基本、最重要的因素。 cnki
The effects of alkali-resistant glass fiber on the expansion, strength and volume stability of cement paste with vary content of high calcium fly ashHFA were studied.
试验研究了在不同高钙粉煤灰掺量下，抗碱玻璃纤维对水泥浆体膨胀、强度和体积稳定性的影响。 cnki
The microstructure of hydrate of cement paste was studied by FTIR reflection spectrum of microscope.
利用红外显微镜反射光谱研究水泥浆体的水化产物微结构。 cnki
The total alkali content and soluble alkali content in cement paste were determined.
测定了水泥浆体中的总碱含量和可溶碱含量。 cnki
The water absorption and desorption properties of two shale ceramisites in water and cement paste were investigated.
研究了两种吸水率不同的陶粒在水中和水泥浆中的吸水返水特性。 dictall
As concrete fine aggregate, it can improve structure of interface between aggregates and cement paste for its reactivity, then can increase the concrete flexural strength.
作为混凝土细骨料，由于其活性可以改善骨料与水泥浆体的界面结构，故可以提高混凝土的抗弯强度； cnki
In this paper, the surface activity , the surface charge the surface treatment and each other effect of inorganic- organic surface about the solvent of clay and cement paste, were di- cussed mainly.
本文主要论述有关粘土矿物和水泥水化物的溶剂亲和性、表面电荷、表面处理以及无机和有机界面化学的相互作用。 cnki
The results show that the degree of hydration of fly ash- cement paste is higher and the porosity is lower than pure Portland cement paste in late ages.
结果表明，与纯硅酸盐水泥相比，粉煤灰水泥水化后期的水化程度较高，浆体总孔隙率较低。 cnki
The results show that SAE significantly improves bending strength of cement paste and cement mortar but reduces their compression strength.
结果表明， SAE的加入使水泥及水泥砂浆的抗折强度有明显的提高，但抗压强度有所降低； chemyq
The instantaneous Young's modulus and Poisson ratio of the cement paste are calculated by the direct average method and two- scale expansion method.
利用本文中模型和均匀化方法直接平均法和二尺度展开法计算了水泥浆体在各瞬时的杨氏模量和泊松比。 cnki
Total porosity of coal gangue cement paste is higher but its pore size at later age is smaller than that of reference cement paste.
与基准水泥浆体相比，煤矸石水泥浆体总孔隙率有所上升，但其孔径后期有所细化。 cnki |