| 释义 |
cast·a·ble 英'kɑːsteɪbl美'kɑːsteɪbl COCA²³⁹¹⁶³
基本例句
adj.可铸的浇铸成形
Adding 7% cordierite, 7% flint clay and2% quartz sand in matrix enabled the castable to have highest thermal shock resistance.
基质中同时引入7%的堇青石、7%的焦宝石和2%的石英砂时，浇注料的抗热震性最好。 cnki
The corrosion behaviors of the different additions to corundum- spinel castable refractory were studied by using static crucible method.
用静态坩埚法研究了加入不同添加剂的刚玉-尖晶石浇注料抗渣侵蚀行为。 cnki
The difference between castable amount per unit volume and bulk density in definition has been pointed out and a method to test castable amount per unit volume has been introduced.
指出了耐火浇注料单位体积用量与体积密度定义上的区别，并且介绍了一种测试耐火浇注料单位体积用量的试验方法。 cnki
The emphasis of discussion lies in slag resistance of castable.
着重对浇注料的抗渣性进行了讨论。 cnki
The experiment results show that the resistance of magnesia- zircon-chrome castable to corrosion and penetration of slag are higher.
实验证明，镁锆铬质浇注料的抗渣侵蚀能力、抗渣渗透能力较高。 cnki
The research of the molding system for the castable polyurethane tire is introduced, mainly including the design and development of the core mold, outer mold and rotatable frame.
介绍聚氨酯浇注轮胎成型系统的研究，主要包括芯模、外模及翻转架的设计和研制。 cnki
The waste integrative casting lid of EAF can be used in the CAS impregnated tube castable after it was crashed and classified.
回收使用过的电炉小炉盖，经过破碎分级后作为原料应用于 CAS浸渍管浇注料中。 dictall
A bauxite spinel castable for furnish is prepared.
研制了矾土尖晶石钢包浇注料。 cnki
Alkali resistant castable refractory was produced using hard clay clinker as main raw material and adding in potash feldspar, ceramic powder etc.
以焦宝石熟料为主要原料，添加钾长石、瓷粉等外加物，制备了耐碱浇注料。 cnki
All of them influence the slag resistances of spinel clinker and its castable refractory.
这些都与尖晶石熟料及铝—尖晶石浇注料的抗渣性有密切关系。 chemyq
In the Iron Plant of WISCO the fast dried castable has been developed and applied into the only sand port of the main runner and a complete set of construction procedure have been established.
武钢炼铁厂在无备用主沟砂口情况下开发、应用了快干浇注料，并摸索出一套施工新工艺。 cnki
Magnesia- alumina spinel is a new type of castable refractory and has been paid attention both at home and abroad.
镁铝尖晶石质浇注料是一种新型耐火浇注料，近年来已受到国内外的高度重视。 cnki
Main wear cause was found by testing and analyzing various properties of castable for tundish. The ways to extend the life of tundish castable were put forward.
通过对中间包永久衬现用浇注料各项性能指标的测定和分析，找出了其损毁的主要原因，提出了延长浇注料寿命的措施。 cnki
Slag resistance experiment was carried out adopting static crucible method, and change regulation of slag resistance performance of high alumina bauxite based- spinel castable was also studied.
同时，采用静态坩埚法进行了抗渣性实验，研究了矾土基高铝-尖晶石浇注料抗渣性能的变化规律。 cnki
The result shows that with the addition of MA spinel, the castable has low water addition, good high temperature strength and volume stability.
结果表明，该浇注料成型用水量少，高温强度高，体积稳定性好。 cnki
The result shows that the properties of the castable can be remarkably improved if the graphite is processed before being used.
结果表明：与含未处理石墨的浇注料相比，含处理石墨浇注料的各项性能都有了很大改善。 chemyq
The work studied the effects of pure calcium aluminate, superfine powders and expansion agent on the physical properties and fluidity of the castable.
研究了纯铝酸钙水泥、二氧化硅和氧化铝混合超细粉及膨胀剂的加入量对浇注料物理性能与流动性的影响。 cnki
The development and application results of refractory castable for cement kiln have been introduced.
本文介绍了水泥窑用耐火浇注料的研究和应用情况。 chemyq
This paper analyzes the problems of GD170 cements with high aluminum refractory castable and expounds the development and use result of the new phosphate with high aluminum refractory castable.
在分析传统 GD170水泥结合高铝浇注料存在问题的基础上，论述了以磷酸盐为结合剂的新型浇注料的研制过程及使用效果。 chemyq
This is because nano- silica can accelerate the sintering process and promote the densification of corundum castable.
这是由于纳米二氧化硅能够促进刚玉浇注料的烧结，使结构致密化所致。 cnki
Through a series of laboratory experiment, padding castable is considered to be good as refractory for the ladle bottom.
通过一系列实验室试验，垫补浇注料可认为是较好的罐底耐火材料。 cnki
When the adding amount of kyanite is4-5%, the castable performance is better.
蓝晶石加入量为4-5%时浇注料的性能较好。 cnki
When the MA spinel addition is15%, the castable has optimal high temperature strength and slag resistance.
当尖晶石加入量为15%时，浇注料具有最佳的高温强度和综合抗渣性能。 cnki |